Home > Precision Alloy >

NiFe Soft Magnetic Materials

Product Categories

FeCrAl Wire [31]
Nichrome Alloy [122]
FeCrAl Alloy [12]
FeCrAl Bar [22]
CuNi Alloy [55]
FeCrAl Strip [19]
Inconel Alloy [145]
Nickel Welding Wire [44]
Pure Nickel Wire [44]
Thermal Spray Wire [12]
Pure Nickel Alloy [16]
Pure Nickel Bar [7]
Hastelloy Alloy [3]
Pure Nickel Tube [16]
Monel Alloy [4]
Pure Nickel Strip [38]
Hastelloy Wire [19]
Incoloy Alloy [15]
Hastelloy Bar [32]
Thermocouple Bare Wire [25]
Hastelloy Tube [11]
Mineral Insulated Cable [17]
Hastelloy Strip [19]
Thermocouple Compensating Wire [19]
Hastelloy Plate [12]
Precision Alloy [44]
Monel Wire [29]
High Temperature Alloy [43]
Monel Bar [22]
Metal Welding Wire [17]
Monel Tube [17]
Metal Foam [17]
Monel Strip [24]
Incoloy Wire [20]
Metal Alloy [14]
Incoloy Bar [14]
Thermocouple Sensors [5]
Incoloy Tube [12]
Incoloy Strip [23]

Changzhou Victory Technology Co., Ltd

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

NiFe Soft Magnetic Materials

Name: NiFe Soft Magnetic Materials
Brand: Victory
Price: 25 USD

Wholesale NiFe Soft Magnetic Materials from china suppliers

Brand Name : Victory

Model Number : Permalloy 80

Place of Origin : China

MOQ : 50

Price : $25-$40

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : 200 tons per month

Delivery Time : 5-21 days

Packaging Details : Standard Export Wooden Cases Ex.Gross Weight Under 20kg=Carton Box/Gross Weight over 20 kg=Plywood Box Or as per Request

Material : NiFe

Certificate : ISO9001

Shape : wire, strip, foil, sheet

Resistivity : 0.56

density : 8.75g/cm3

size : customized

Standard : GB/ASTM/AISI/ASME

Condition : Bright, Annealed, Soft

Application : Industrial Magnet

Curie Point : 400℃

HCR : 30

Feature : high initial permeability

Contact Now

High Permeability Soft Magnetic Alloy

NiFe Soft Magnetic Materials

This text describes a high nickel alloy that has a tendency to "gummy" machining. It behaves similarly to the austenitic (300 series) stainless steels. When machining this alloy, high-speed steel or carbide tools may be used with a lard oil lubricant. However, if water-soluble cutting fluids are used, it's important to clean the parts thoroughly immediately after machining to avoid corrosion contamination.

When using high-speed steel tooling, turning should be done at a speed of 50 surface ft./min. with a feed of .001" to .002" per revolution. Drilling should be done at a speed of 35 surface ft./min. with a feed of .001" to .004" per revolution.

This alloy can be readily formed using standard methods and can be welded using conventional welding methods. However, it's not hardenable by heat treatment. Annealing may be done in a dry hydrogen atmosphere at 2150 F for 4 hours, followed by furnace cooling to 1100 F, then a cooling rate of 500 F per hour from 1100 F to 700 F. After reaching 700 F, it should be air-cooled. A strain relief anneal may be done at 1700 F for 1/2 hour in a dry hydrogen or inert gas atmosphere.

The alloy has good ductility and is easily cold formed. Strip in the cold rolled condition works best for blanking operations. It's worth noting that this alloy can only be hardened by cold working.

Applications

High sensitivity and small power transformers, magnetic amplifiers, relays, chokes, magnetic heads for magnetic recording devices, magnetic shields, various tape wound cores, cut cores, and laminated cores used in weak magnetic fields.

Material	C	P	S	Mn	Si	Ni	Cr	Co	Mo	Cu	Fe
	Max
Permalloy80	0.03	0.020	0.020	0.3-0.6	0.15-0.30	79.0-81.0	-	-	4.8-5.2	≤0.2.	Rest

rial	Shape	Class	Thickness or Diameter mm	Magnetic permeability in 0.08A/m magnetic field intensity μ0.4(mH/m)	Maximum permeability μm(mH/m)	Coercivity(under saturation magnetic induction)Hc/A·m-1	Saturation magnetic induction Bs/T
				not less than		no greater than
Permalloy80	Cold rolled strip	Ⅰ	0.03-0.04	18000(22.5)	80000(100)	3.6	0.70
			0.05-0.09	28000(35)	110000(137.5)	2.4	0.70
			0.10-0.19	30000(37.5)	150000(187.5)	1.6	0.70
			0.20-0.34	40000(50)	180000(225)	1.2	0.70
			0.35-1.00	50000(62.5)	250000(312.5)	0.8	0.70
			1.10-2.50	40000(50)	150000(187.5)	1.2	0.70
		Ⅱ	0.03-0.04	30000(37.5)	110000(137.5)	2.4	0.70
			0.05-0.09	40000(50)	140000(175)	1.6	0.70
			0.10-0.19	50000(62.5)	180000(225)	1.2	0.70
			0.20-0.34	60000(75)	200000(250)	1.0	0.70
			0.35	55040(68.8)	260000(325)	0.7	0.70
	Hot rolled tape		4.5-20	30000(37.5)	100000(125)	1.6	0.70
	Hot forged bar		20-100	30000(37.5)	100000(125)	1.6	0.70

Material	Shape	Class	Thickness or Diameter mm	Magnetic permeability in 0.08A/m magnetic field intensity μ0.4(mH/m)	Maximum permeability μm(mH/m)	Coercivity(under saturation magnetic induction)Hc/A·m-1	Saturation magnetic induction Bs/T
				not less than		no greater than
Permalloy80	Cold rolled strip	Ⅰ	0.03-0.04	18000(22.5)	80000(100)	3.6	0.70
			0.05-0.09	28000(35)	110000(137.5)	2.4	0.70
			0.10-0.19	30000(37.5)	150000(187.5)	1.6	0.70
			0.20-0.34	40000(50)	180000(225)	1.2	0.70
			0.35-1.00	50000(62.5)	250000(312.5)	0.8	0.70
			1.10-2.50	40000(50)	150000(187.5)	1.2	0.70
		Ⅱ	0.03-0.04	30000(37.5)	110000(137.5)	2.4	0.70
			0.05-0.09	40000(50)	140000(175)	1.6	0.70
			0.10-0.19	50000(62.5)	180000(225)	1.2	0.70
			0.20-0.34	60000(75)	200000(250)	1.0	0.70
			0.35	55040(68.8)	260000(325)	0.7	0.70
	Hot rolled tape		4.5-20	30000(37.5)	100000(125)	1.6	0.70
	Hot forged bar		20-100	30000(37.5)	100000(125)	1.6	0.70

NiFe Soft Magnetic Materials